NO |
properties |
unit |
standard |
result |
1 |
appearance |
|
The sample powder of phenolic molding compound should not contain impurities and dirt, and the sample has bright and smooth surface |
accord with |
2 |
Volume factor |
|
≤4.0 |
2.09 |
3 |
Relative density |
g/cm³ |
≤2.0 |
1.41 |
4 |
Impact strength |
KJ/m2 |
≥3.5 |
6.05 |
5 |
Hot deformation temperature |
℃ |
≥160 |
175 |
6 |
Bending strength |
MPa |
≥80 |
88 |
7 |
Insulation resistance |
Ω |
≥1010 |
1.33*1010 |
8 |
Dielectric strength |
MV/m |
≥2.0 |
3.04 |
9 |
Dielectric loss factor |
|
/ |
/ |
10 |
Water absorption |
mg |
≤40 |
14.6 |
11 |
Shrinkage |
% |
Negotiation between the supplier and the demander |
0.54 |
12 |
Mobility |
mm |
Negotiation between the supplier and the demander |
155 |
13 |
Tracking resistance index |
|
≥175 |
175 |
14 |
Combustion performance (hot rod method) |
|
After 3min, the hot rod should leave the sample, and there should be no visible flame within 30s |
accord with |
The data are for reference only